Study on Microstructure Refinement of Weld Metal and Property of HAZ for High Strength Al-Cu Alloy;

The results indicate that HAZ produced during welding of grade X80 steel is made up of grads structure under different temperature.

并利用显微组织变化和电化学理论分析了焊缝试样HAZ的SCC机理。

The Ni based alloy powder surfacing layer was obtained by light beam surfacing on the 45 steel and the microstructure of heat affected zone(HAZ) and the phase of the surfacing layer were studied.

Hardness measurement on welding thermal simulated specimens and cross weld specimens showed that no softening occurred in the HAZ. All the cross weld tensile specimens ruptured in the base metal.

采用斜y形坡口焊接裂纹试验和HAZ最大硬度试验评定了JB800贝氏体钢的冷裂纹敏感*。

无论是焊接热模拟试件还是焊接接头硬度测试均表明HAZ不存在软化问题，接头拉伸试验断在远离热影响区的母材上。

Study on Crystallizing Procedure and HAZ by Plasma Beam Cladding;

Influence of thermal cycle on impact toughness of HAZ of high-Nb pipeline steel

Simulation of Grain Growth in the HAZ of Industrial Pure Aluminum;

Effect on HAZ Structure and Toughness of Welding Thermal Cycle for High Nb X70 Grade Pipeline Steel

The results show that toughness of the coarse grained HAZ is improved after second welding heat cycle except intercritical two-phase heating.

Fatigue specimens cracked at two-sided through-thickness sheet, fatigue crack appeared initially in HAZ of inner surface of lap plates, along the thickness direction extended to outer surface;

According to the requirements of the standard,the specimen is a standard TPB (three point bending) shape that has a rectangular section of B×2B and notch orientation of NP. the results were calculated by using the P V curves of parent material,weld metal and HAZ (heat affected zone).

Research on Microstructure and Toughness in Simulative Welding HAZ of 08MnNiVR Oil Tank Steel

Computer Simulation of Austenite Grain Growth in HAZ of Ultra-Fine Grain Steel;

Thirdly, Through Y-slit type cracking test and HAZ maximum hardness test the paper assesses the cold crack sensitivity of JB800 bainite steel.

取尺寸为B× 2B(B为试样厚度 )、缺口方向为Np的试样进行三点弯曲试验 ,然后由所得到的 0℃下母材、焊缝和热影响区 (HAZ)的p -V曲线来计算CTOD值 ,并对试验结果进行了讨论和总结。

The mechanism of SCC in HAZ of specimens was analyzed by the microstructure variation and electrochemical theory.

Fracture toughness of heat-affected zone( HAZ) was between the base metal and weld metal.

利用本文所建模型，结合JB800贝氏体钢的SH - CCT图，成功实现了对JB800贝氏体钢HAZ组织和硬度的预测。